Galil (Gold)
Smith-Emery Test Results
Technical Information | ASTM Test Method | Value |
---|---|---|
Absorption By Weight% | C97 | 1.17 |
Density, lbs./cu. ft | C97 | 158 |
Static Coefficient of Friction-Wet | C1028-89 | 0.81 |
Static Coefficient of Friction-Dry | C1028-89 | 0.79 |
Flexural Strength, psi | C880-M | 1529 |
Law Engineering & Environmental Services Tests
Technical Information | ASTM Test Method | Value |
---|---|---|
Absorption By Weight% | C 373-88 | 0.74 |
Static Coefficient of Friction-Wet | C1028-89 | 0.58 |
Static Coefficient of Friction-Dry | C1028-89 | 0.79 |
Wear Index | C501-84 | 16.1 |
Breaking Strength | C648-84 | 647.0 |
MOH’s Hardness | MOH’s Hardness Procedure | 4.0 |
Wear Index | C501-84 | 11.9 |
Hebron White
Smith-Emery Test Results
Technical Information | ASTM Test Method | Value |
---|---|---|
Absorption By Weight% | C97 | 0.78 |
Density, lbs./cu. ft | C97 | 164 |
Static Coefficient of Friction-Wet | C1028-89 | 0.81 |
Static Coefficient of Friction-Dry | C1028-89 | 0.79 |
Flexural Strength, psi | C880-M | 1,529 |
Compressive Strength, psi | C170 | 11,289 |
Abrasion Resistance, Hardness | C241 | 10.5 |
Law Engineering & Environmental Services Tests
Technical Information | ASTM Test Method | Value |
---|---|---|
Absorption By Weight% | C 373-88 | 1.62 |
Static Coefficient of Friction-Wet | C1028-89 | 0.55 |
Static Coefficient of Friction-Dry | C1028-89 | 0.75 |
Wear Index | C501-84 | 11.9 |
Breaking Strength | C648-84 | 645.0 |
MOH’s Hardness | MOH’s Hardness Procedure | 4.0 |
Hebron Pink
Smith-Emery Test Results
Technical Information | ASTM Test Method | Value |
---|---|---|
Absorption By Weight% | C97 | 0.72 |
Density, lbs./cu. ft | C97 | 164 |
Static Coefficient of Friction-Wet | C1028-89 | 0.81 |
Static Coefficient of Friction-Dry | C1028-89 | 0.79 |
Flexural Strength, psi | C880-M | 1,529 |
Compressive Strength, psi | C170 | 11,380 |
Abrasion Resistance, Hardness | C241 | 10.5 |
Law Engineering & Environmental Services Tests
Technical Information | ASTM Test Method | Value |
---|---|---|
Absorption By Weight% | C 373-88 | 0.72 |
Static Coefficient of Friction-Wet | C1028-89 | 0.59 |
Static Coefficient of Friction-Dry | C1028-89 | 0.782 |
Wear Index | C501-84 | 13.7 |
Breaking Strength | C648-84 | 645.0 |
MOH’s Hardness | MOH’s Hardness Procedure | 4.0 |
Ramon Gray
Smith-Emery Test Results
Technical Information | ASTM Test Method | Value |
---|---|---|
Absorption By Weight% | C97 | 0.86 |
Density, lbs./cu. ft | C97 | 163 |
Static Coefficient of Friction-Wet | C1028-89 | 0.78 |
Static Coefficient of Friction-Dry | C1028-89 | 0.74 |
Flexural Strength, psi | C880-M | 1,254 |
Ramon Gold
Smith-Emery Test Results
Technical Information | ASTM Test Method | Value |
---|---|---|
Absorption By Weight% | C97 | 0.78 |
Density, lbs./cu. ft | C97 | 169 |
Flexural Strength, psi | C880-M | 1,248 |
Compressive Strength, psi | C170 | 11,490 |
Abrasion Resistance, Hardness | C241 | 10.5 |